| | 55 – 60 MPa
(8,000 – 8,700 psi) | |
| | | |
| | 2,600 – 3,000 MPa
(375,000 – 435,000 psi) | 2100-2800
(305,000-405,000 psi) |
| | 65 – 75 MPa
(9,500 – 11,000 psi) | |
| | 1,700 – 2,200 MPa
(245,000 – 320,000 psi) | 1600-1800
(230,000-260,000 psi) |
| | 58 – 68 °C
(136 – 154 °F) | |
HDT, oC @ 0.45MPa after thermal post
treatment procedure A | | 82 – 90 °C
(180 – 194 °F) | |
HDT, oC @ 0.45MPa after thermal post
treatment procedure B | | 92 – 95 °C
(198 – 203 °F) | |
| | 51 – 55 °C
(124 – 131 °F) | |
| | 90 – 115 J/m
(1.69 – 2.15 ft lb/in) | 90-100
(1.69-1.87 ft lb/in) |
| | 47 – 53 °C
(117 – 127 °F) | |
| | | |
| | | |
| | | |